Novel cerium oxide nanocomplex and a composition for preventing or treating peritonitis comprising the same

ABSTRACT

A cerium oxide nanocomplex, a composition containing the cerium oxide nanocomplex as an active ingredient, and uses thereof for preventing or treating peritonitis are disclosed. The cerium oxide nanocomplex improves the biomedical stability, biocompatibility, and efficiency of the production process of nanoparticles while maintaining the excellent inhibitory activity against inflammation by applying a biocompatible polymer composed of an optimal combination. The cerium oxide nanocomplex may be used as an excellent therapeutic composition that may greatly improve patients&#39; survival rate by effectively inhibiting inflammatory response and quickly blocking tissue damage at early stage of peritonitis when a radical inflammatory injury occurs because of the penetration of bacteria, foreign body and immune cells into a perforated organ in the abdominal cavity.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims benefit based on U.S. Provisional App. No. 63/247,563 filed Sep. 23, 2021, of which the entire content is incorporated by reference herein.

TECHNICAL FIELD

The present disclosure relates to a cerium oxide nanocomplex coated with a biocompatible dispersion stabilizer and a composition for preventing or treating peritonitis, containing cerium oxide nanocomplex as an active ingredient.

BACKGROUND ART

Nanoparticles, which have been applied for various purposes in the field of diagnosis and treatment, exhibit new physical/chemical properties different from bulk materials in vivo due to their nanoscale size. Currently, many studies on the nanoparticles have been conducted and in this regard, vigorous efforts have been made to develop nanoparticles that exhibit optimal properties suitable for medical use by adjusting the particles' composition, shape, size, and properties, etc. as appropriate to the purpose.

Cerium oxide has thermal stability at high temperature and has a redox reaction of Ce⁴⁺/Ce³⁺ depending on the surrounding oxygen concentration due to its lattice structure, and thus has had various applications such as electrolytes of solid batteries, compositions for UV filters, oxygen sensors, optical devices, etc. Especially in the medical field, cerium oxide has been spotlighted as a therapeutic composition for a wide range of diseases caused by oxidative stress and inflammation due to its excellent ability to scavenge reactive oxygen species.

With a common method for the synthesis of cerium oxide nanoparticles, it is not only difficult to uniformly distribute the particles in a nanoscale, but also it is not easy to synthesize the particles in a fine size of 10 nm or less. For example, cerium oxide nanoparticles synthesized through a hydrothermal method, which is one of the aqueous phase-based methods, usually have a size ranging from several hundred nm to several microns, and because of this, it is difficult to precisely control the particle size and the particles show poor dispersibility. Therefore, methods for preparing cerium oxide nanoparticles having a smaller average particle size and a uniform size distribution have been proposed, but these methods are not suitable for industrial bulk production because they require an inefficient process involving a high-temperature processing at hundreds of °C.

Accordingly, there is a need to develop a new method that may efficiently produce cerium oxide nanoparticles that have a size of 50 nm or less, uniform size distribution and good dispersibility, are facile to produce and maintain a unique antioxidant effect in a moderate reaction condition.

Meanwhile, peritonitis refers to an inflammatory condition in the peritoneum. This peritoneal inflammation is caused by an abdominal infection through bowel perforation. When a bowel perforation occurs as a result of various medical conditions such as trauma, infection, inflammatory disease, ulcer, cancer, etc., microbes and other intestinal contents spill into the abdomen, marking the initial onset of peritonitis. During the early stage of peritonitis, granulocytes, mononuclear cells and macrophages activate an inflammatory response to cause inflammatory injury in the peritoneum and this is when the peritoneal permeability increases. Failure to treat inflammation properly at this stage can cause inflammatory mediator, bowel bacteria, endotoxin, etc. to leak into the blood. This activates endothelial cells, neutrophils, and monocytes in the circulation and the massive release of cytokine can cause a severe systemic inflammatory response, which then leads to sepsis and multiple organ failure (MOF) that can result in death.

The treatment of bowel perforation peritonitis mainly involves antibiotics, or laparotomy and conservation therapy. Meanwhile, no drug has been developed yet to directly inhibit the inflammatory response at the early stage of peritonitis, which calls for the development of a novel anti-inflammatory therapeutic composition that can effectively inhibit inflammation.

A number of papers and patent documents are referenced throughout the present specification and citations thereof are shown. The disclosure of the cited papers and patent documents is incorporated herein by reference in their entirety to more clearly describe the level of the technical field to which the present disclosure pertains and the content of the present disclosure.

DISCLOSURE Technical Problem

The present inventors have made intensive efforts to develop a nanoparticle-based therapeutic composition that can effectively inhibit initial inflammatory response triggered by various causes of infection or inflammation including bowel perforation. As a result, the present disclosure has been completed by finding that when a polymer layer in which a monomer of a pyrrolidone derivative of Formula 1 is repeated is formed on the core of the cerium oxide nanoparticles, the biomedical stability, biocompatibility and efficiency of production process of nanoparticles were further improved while the peritoneal inflammatory response caused by the influx of bacteria or foreign body reaction was effectively inhibited by nanoparticles, which shows that the present nanoparticles may be used as excellent therapeutic composition that may significantly improve the survival rate of individuals and minimize tissue damage by effectively inhibiting inflammation in the peritoneum.

Thus, an object of the present disclosure is to provide a composition that prevents or treats peritonitis, containing a cerium oxide nanocomplex.

Other objects and advantages of the present disclosure will be made clearer by the following detailed description of the disclosures, claims and drawings.

Technical Solution

In an aspect, there is provided a composition for preventing or treating peritonitis, comprising a cerium oxide nanocomplex as an active ingredient comprising:

-   (a) Core layer of cerium oxide nanoparticles; and

-   (b) an inner layer including a polymer represented by the following     Formula 1.

-   

-   wherein R₁ and R₂     are each independently hydrogen or oxygen, represents a single bond     or a double bond, I is 1 or 2, and m is an integer of 100 to 1000.

The present inventors have made intensive efforts to develop a nanoparticle-based therapeutic composition that can effectively inhibit initial inflammatory response triggered by various causes of infection or inflammation including bowel perforation. As a result, the present inventors have found that when a polymer layer in which a monomer of a pyrrolidone derivative of Formula 1 is repeated is formed on the core of the cerium oxide nanoparticles, the biomedical stability, biocompatibility and efficiency of production process of nanoparticles were further improved while the peritoneal inflammatory response caused by the influx of bacteria or foreign body reaction was effectively inhibited by nanoparticles, which shows that the present nanoparticles may be used as excellent therapeutic composition that may significantly improve the survival rate of individuals and minimize tissue damage by effectively inhibiting inflammation in the peritoneum.

In particular, as seen from the examples described later in Examples section, the nanocomplex of the present disclosure can stably and economically bulk-produce uniform and fine particles for a sufficient reaction time without a harsh environment such as a strong base and strong acid condition at a high temperature. The related art requires a strong acid/strong base such as HCl and NaOH at a high temperature of 95° C. for an extremely short reaction time within 1 minute because polyethylene glycol (PEG) or a PEG derivative modified with a succinimidyl group is mainly used in order to ensure stability in vivo in the synthesis process of the cerium oxide nanoparticles, and thus has suffered great difficulties in obtaining a large amount of uniform particles. However, the nanocomplex according to the present disclosure secures stable synthesis conditions such as a reaction time of about 2 hours at 70° C., but also does not require a strong acid or strong base environment and thus, has effectively overcome the disadvantages of the related art.

As used herein, the term “core layer” refers to an innermost layer having only one surface in contact with other layers in a multilayer composite.

As used herein, the term “multilayer composite” refers to a composite consisting of a plurality of layers composed of different components, and includes, without limitation, a laminated multilayer structure, a core-shell multilayer structure, and combinations thereof. Specifically, the multilayer composite according to the present disclosure has a core-shell type multilayer structure in which nanoparticles are present at the center and the polymer of Formula 1 and a biocompatible dispersion stabilizer surround the nanoparticles on the outer shell.

The process where a polymer represented by Formula 1 is formed by surrounding the core of the cerium oxide nanoparticle can be achieved by coating the polymer represented by Formula 1 on the surface of core layer.

As used herein, the term “coating” refers to forming a new layer having a certain thickness by applying a specific material on a target surface, and the target surface and the coating material may be coated through ionic or non-covalent bond. The term “non-covalent bond is a concept that includes not only physical bonds such as adsorption, cohesion, entanglement, and entrapment, but also bonds in which the interaction such as hydrogen bonds and van der Waals bonds occurs alone or in combination with the physical bonds described above. When coated with the polymer of formula 1, a closed layer may be formed while completely surrounding the surface to be modified, or may form a partially closed layer.

As used herein, the term “polymer” refers to a synthetic or natural polymer compound in which the same or different types of monomers are continuously linked. Thus, the polymer includes a homopolymer (a polymer in which one type of monomer is polymerized) and an interpolymer prepared by the polymerization of at least two different monomers, wherein the interpolymer includes both a copolymer (a polymer prepared from two different monomers) and a polymer prepared from more than two different monomers. Specifically, the polymer of Formula 1 used in the present disclosure is a homopolymer.

As used herein, the term “alkyl” refers to a straight or branched chain, saturated hydrocarbon group, and includes, for examples, methyl, ethyl, propyl, isopropyl, etc. C₁-C₃ alkyl refers to an alkyl group having an alkyl unit having 1 to 3 carbon atoms, and when C₁-C₃ alkyl is substituted, the number of carbon atoms in the substituent is not included.

As used herein, the term “biocompatibility” refers to a property of not causing short-term or long-term side effects when administered in vivo and in contact with cells, tissues or body fluids of organs, and specifically, refers to not only tissue compatibility and blood compatibility that do not cause tissue necrosis or blood coagulation in contact with biological tissue or blood, but also biodegradability, which is a property of being disappeared after a certain period of time after in vivo administration of the material, and “excretability, which is a property of being excreted outside the body without accumulation after in vivo administration of the material.” Thus, the term “biocompatible dispersion stabilizer” refers to a component that improves the dispersibility of particles while having the biocompatibility described above.

As used herein, the term “biodegradability” refers to a property of the material to naturally decompose when exposed to a physiological solution having a pH of 6 to 8, and specifically, refers to a property in which the material may be decomposed over time by body fluids, decomposing enzymes, or microorganisms, etc., in vivo.

According to a specific embodiment of the present disclosure, the cerium oxide nanoparticles used in the present disclosure may be cerium(IV) oxide (CeO₂), cerium(III) oxide (Ce₂O₃), or a mixture thereof.

According to a specific embodiment of the present disclosure, in Formula 1, R₁ is hydrogen, R₂ is oxygen, and I is 1. According to an octet rule, it is obvious that when R1 is hydrogen,

is a single bond, and when R₂ is oxygen,

is a double bond. The compound of Formula 1 wherein R₁ is hydrogen, R₂ is oxygen, and I is 1 is polyvinylpyrrolidone (PVP).

According to a specific embodiment of the present disclosure, the nanocomplex of the present disclosure further comprises an outer layer that comprises one or more biocompatible dispersion stabilizers selected from the group consisting of polyglutamic acid (PGA), poly(aspartic acid)(PASP), alginate, poly(acrylic acid) (PAA), poly(methacrylic acid) (PMAA), poly(methyl methacrylic acid), poly(maleic acid) (PMA), poly(butadiene/maleic acid) (PBMA), poly(vinylphosphonic acid) (PVPA), poly(styrenesulfonic acid) (PSSA), polyvinyl alcohol (PVA) and dextran.

As used herein, the term “inner layer” refers to a layer closer to the core than the outer layer, and the term “outer layer” refers to a layer that surrounds the inner layer of a core-shell structure and is further away from the core than the inner layer. The inner layer does not necessarily have to be a layer in direct contact with the core layer and an additional layer closer to the core layer than the inner layer may be present. The outer layer also does not necessarily have to be an outermost layer, and the outermost layer located farther away from the core than the outer layer may be further present.

According to the present disclosure, the boundary between the core layer and the inner layer is clearly distinguished, but the boundary between the inner layer and the outer layer may or may not be clearly distinguished. If a boundary between the inner layer and the outer layer is not clear, each component of the inner layer and the outer layer may be mixed in the vicinity of the interface or in the entire section.

According to a specific embodiment of the present disclosure, the biocompatible dispersion stabilizer included in the outer layer is polyglutamic acid (PGA). Polyglutamic acid (PGA) may be poly-α-glutamic acid, poly-β-glutamic acid, or poly-γ-glutamic acid, specifically poly-α-glutamic acid. Most specifically, the poly-α-glutamic acid is poly(L-glutamic acid) (PLGA).

According to a specific embodiment of the present disclosure, the nanocomplex according to the present disclosure further includes a multifunctional ligand represented by the following Formula 2:

wherein n is an integer of 3 to 7.

As used herein, the term “multi-functional ligand” refers to a molecule having two or more active functional groups and binding to two or more molecules, thereby serving as a linker between the molecules. The multi-functional ligand of Formula 2 used in the present disclosure has a carboxyl group capable of binding to cerium oxide nanoparticles and an amine group capable of binding to PVP in the inner layer and/or PGA, PVA or dextran in the outer layer to enable the nanocomplex according to the present disclosure to be formed more efficiently and stably.

Specifically, in the above Formula 2, n is 5. The compound of Formula 2 wherein n is 5 is 6-aminohexanoic acid (6-AHA).

According to a specific embodiment of the present disclosure, the nanocomplex according to the present disclosure has an average particle size of 5 nm to 100 nm. The nanocomplex has an average particle size of more specifically 5 nm to 80 nm, and most specifically 5 nm to 50 nm.

As used herein, the term “peritonitis” refers to an inflammation in peritoneum, a thin membrane that lines the abdominal cavity and organs contained therein. When an inflammation occurs in the abdominal cavity due to any cause, the bowel fluids, fibrin, immune cells, pus, etc. build up in the abdominal cavity, leading to abdominal pain and high fever. The peritonitis may progress to an acute or a chronic one and may be localized or generalized.

According to a specific embodiment of the present disclosure, the peritonitis that may be prevented or treated by the present disclosure is perforative peritonitis.

As used herein, the term “perforative peritonitis” refers to a condition of peritoneal infection and inflammation caused when pathogens penetrate into the sterile peritoneal cavity or when bodily fluids such as blood, bile or urine, etc. spill into the abdominal cavity through a perforation in an abdominal organ that includes esophagus, stomach, duodenum, small intestine, large intestine, appendix and gallbladder.

Also, the present disclosure may effectively control peritoneal inflammation triggered by other causes therefore, the peritonitis that may be prevented or treated may be non-perforative peritonitis.

As used herein, the term “non-perforative peritonitis” refers to a peritonitis that either does not accompany perforation of an organ in the abdomen, or does not directly or indirectly caused by perforation of an organ in the abdomen.

As used herein, the term “prevention” refers to inhibiting the development of a disease or condition in a subject who has not been diagnosed with the disease or condition, but is likely to be afflicted with such a disease or illness.

As used herein, the term “treatment” refers to (a) inhibiting the progression of the disease, illness, or symptom; (b) alleviating the disease, illness, or symptom; or (c) eliminating the disease, illness, or symptom. The composition according to the present disclosure reduces reactive oxygen species to inhibit, eliminate or alleviate the progress and development of inflammatory response, specifically peritoneal inflammation caused by bowel perforation. Thus, the composition according to the present disclosure may itself be a composition for treating these diseases, or may be administered in conjunction with other pharmacological ingredients having an anti-inflammatory effect and applied as a therapeutic adjuvant for the above diseases. Accordingly, as used herein, the term “treatment” or “therapeutic agent” includes the meaning of “therapeutic aid” or a “therapeutic adjuvant.”

As used herein, the term “administration” refers to administration of a therapeutically effective amount of the composition according to the present disclosure directly to a subject so that the same amount is formed in the body of the subject, and has the same meaning as “transplantation” or “injection.”

As used herein, the term “therapeutically effective amount” refers to the amount of the composition contained in an amount sufficient to provide a therapeutic or prophylactic effect to an individual who wishes to administer the composition according to the present disclosure, and is therefore meant to include “prophylactically effective amount.”

As used herein, the term “subject” includes, without limitation, human, mouse, rat, guinea pig, dog, cat, horse, cow, pig, monkey, chimpanzee, baboon, or rhesus monkey. Specifically, the subject is a human.

When the composition according to the present disclosure is prepared as a pharmaceutical composition, the pharmaceutical composition according to the present disclosure contains a pharmaceutically acceptable carrier. Pharmaceutically acceptable carriers contained in the pharmaceutical composition according to the present disclosure are commonly used in preparation, and examples thereof include, but are not limited to, lactose, dextrose, sucrose, sorbitol, mannitol, starch, acacia gum, calcium phosphate, alginate, gelatin, calcium silicate, microcrystalline cellulose, polyvinylpyrrolidone, cellulose, water, syrup, methyl cellulose, methyl hydroxybenzoate, propyl hydroxybenzoate, talc, magnesium stearate, and mineral oil, etc. The pharmaceutical composition according to the present disclosure may further contain lubricants, wetting agents, sweetening agents, flavoring agents, emulsifying agents, suspending agents, preservatives, etc., in addition to the above components. Suitable pharmaceutically acceptable carriers and formulations are described in detail in Remington’s Pharmaceutical Sciences (19th ed., 1995).

The pharmaceutical composition according to the present disclosure may be administered through various routes of administration, specifically, parenterally, and more specifically, orally, intravenously, intraarterially, subcutaneously, intraperitoneally, intradermally, intramuscularly, intraventricularly, intrathecally, inhalationally, nasally, intraarticularly, or topically.

A suitable dosage of the pharmaceutical composition according to the present disclosure may be variously prescribed depending on factors such as formulation method, administration mode, age, weight, sex, pathological condition, food, administration time, administration route, excretion rate, and response sensitivity of the patient. A preferred dosage of the pharmaceutical composition according to the present disclosure is within the range of 0.0001 to 100 mg/kg for adults.

The pharmaceutical composition according to the present disclosure may be prepared in unit dosage form by formulating with a pharmaceutically acceptable carrier and/or excipient, or may be prepared by introduction into a multi-dose container, according to a method that may be easily carried out by a person of ordinary skill in the art to which the present disclosure pertains. In this case, the preparation may be in the form of solutions, suspensions, syrups, or emulsions in oil or aqueous medium, or may also be in the form of extracts, powders, granules, tablets or capsules, and may additionally include dispersants or stabilizers.

Advantageous Effects

The features and advantages of the present disclosure are summarized as follows:

-   (a) the present disclosure provides a cerium oxide nanocomplex, a     method for preparing the same, and a composition for preventing or     treating peritonitis, containing the cerium oxide nanocomplex as an     active ingredient, and -   (b) the present disclosure may be usefully used as an efficient     nanoparticle therapeutic composition by applying a biocompatible     polymer composed of an optimal combination to significantly improve     the biomedical stability, biocompatibility, and efficiency of the     production process of nanoparticles while maintaining excellent     inhibitory activity against inflammation. -   (c) the present disclosure, in particular, may be usefully used as     an excellent therapeutic composition that may greatly improve     patients' survival rate by effectively inhibiting inflammatory     response and quickly blocking tissue damage at the early stage of     peritonitis when a radical inflammatory injury occurs because of the     penetration of bacteria, foreign body and immune cells into a     perforated organ in the abdominal cavity. Thus, the present     disclosure may be applied as a fundamental therapeutic agent that     enables early inhibition of inflammatory response, replacing the     conventional symptomatic therapies such as antibiotics and bowel     perforation laparotomy.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram illustrating a transmission electron microscope image of a cerium oxide nanocomplex according to the present disclosure.

FIG. 2 is a diagram illustrating results of analyzing the shape and dispersion of the cerium oxide nanocomplex depending on the properties of the solvent.

FIG. 3 is a diagram illustrating a particle size change of the cerium oxide nanocomplex depending on whether or not the compound is present.

FIG. 4 is a diagram illustrating results of analyzing the particle size change depending on the amounts of polyvinyl pyrrolidone.

FIG. 5 is a diagram illustrating results of analyzing the particle size for each reaction time of the cerium oxide nanocomplex using a dynamic light scattering device.

FIG. 6 a is a diagram showing results of checking whether or not the cerium oxide nanocomplex are coated with a biocompatible dispersion stabilizer using a surface potential analysis device. FIG. 6 b illustrates results of analyzing the particle size of the cerium oxide nanocomplex using a dynamic light scattering device.

FIG. 7 a and FIG. 7 b are diagrams illustrating the evaluation results of hydrogen peroxide and hydroxyl radical scavenging capacity of the cerium oxide nanocomplex.

FIG. 8 is a diagram illustrating the improvement in survival rate in a mouse model of cecal ligation and puncture by administering the cerium oxide complex of the present disclosure.

FIG. 9 is a graph showing the comparison results of chronological clinical symptom scores of each mouse in the experiment of FIG. 8 .

BEST MODE

Hereinafter, the present disclosure will be described in detail with reference to the following examples. These examples are only for illustrating the present disclosure in more detail, and it will be apparent to those of ordinary skill in the art that the scope of the present disclosure.

EXAMPLES Examples 1: Synthesis of Cerium Oxide Nanocomplex

A first solution was prepared by dissolving 6-aminohexanoic acid (6-AHA) (0.65585 g, Sigma-Aldrich, St. Louis, MO) in deionized water (30 mL). A third solution was prepared by adding a second solution in which polyvinylpyrrolidone (PVP) (2.0 g, Sigma-Aldrich, St. Louis, MO) was dissolved in ethyl alcohol (25 mL) and heating the second solution to 70° C. in air while stirring the first solution. Meanwhile, a fourth solution was prepared by dissolving cerium(III) nitrate hexahydrate (Ce(NO₃)₃·6H₂O, 0.540 g, Alfa Aeser, Ward Hill, MA) in ethyl alcohol (50 mL) at room temperature (about 20° C.). Thereafter, a fifth solution was prepared by adding the fourth solution to the third solution. Then, the temperature of the fifth solution was maintained at 70° C. for 2 hours, and then cooled to room temperature (about 20° C.). Through such a process, cerium oxide nanoparticles in which 6-aminohexanoic acid and polyvinyl pyrrolidone were bound to the surface, were obtained (FIG. 1 ). Next, the cerium oxide nanoparticles were washed three times with acetone to remove unreacted materials.

Example 2: Synthesis Trend of Cerium Oxide Nanocomplex Depending On Solvent

In order to identify the formation tendency of particles depending on the synthetic solvent, the formation state of the cerium oxide nanocomplex was confirmed by using a 100% aqueous solvent or a 70% ethyl alcohol solvent.

# 100% Aqueous Solvent

A first solution was prepared by dissolving 6-aminohexanoic acid (0.65585 g, Sigma-Aldrich, St. Louis, MO) in deionized water (30 mL), and a third solution was prepared by adding a second solution in which polyvinylpyrrolidone (2.0 g, Sigma-Aldrich, St. Louis, MO) was dissolved in deionized water (25 mL) during stirring of the first solution, and then heating the second solution to 70° C. in air. Meanwhile, a fourth solution was prepared by dissolving cerium(III) nitrate hexahydrate (Ce(NO₃)₃·6H₂O, 0.540 g, Alfa Aeser, Ward Hill, MA) in deionized water (50 mL) at room temperature (about 20° C.). Thereafter, a fifth solution was prepared by adding the fourth solution to the third solution. Then, the temperature of the fifth solution was maintained at 70° C. for 2 hours, and then cooled to room temperature (about 20° C.) to obtain cerium oxide nanoparticles in which 6-aminohexanoic acid and polyvinylpyrrolidone were bonded to the surface. Next, the cerium oxide nanoparticles were washed three times with acetone to remove unreacted materials.

# 70% ethyl alcohol solvent: The solvent was obtained in the same manner as in the Example 1.

As the result of analyzing the transmission electron microscopy image, it could be confirmed that the cerium oxide nanocomplex synthesized with 100% aqueous solvent was difficult to identify the individual dispersibility of the particles, and was entangled with each other and aggregated like a spider web, whereas the cerium oxide nanocomplex synthesized with 70% ethyl alcohol solvent had high dispersibility of particles (FIG. 2 ). It was found from the above results that the alcohol solvent is more advantageous than the aqueous solvent in terms of the reaction rate and stable dispersibility of the particles.

Example 3: Structure Formation of Cerium Oxide Nanocomplex Depending On Components of Synthesis Reactant

In order to confirm a structural change of the nanocomplex depending on whether or not 6-aminohexanoic acid and polyvinyl pyrrolidone is present during a synthesis process, 6-AHA and PVP were sequentially excluded from the synthesis process of Example 1, and finally, the experiment was conducted in a form including all additives. The particle size was analyzed using dynamic light scattering device.

As a result, it was confirmed that no particles were formed in the absence of 6-AHA, and very large particles of 100 nm or more were formed in the absence of PVP, whereas uniform particles of 10 nm size were synthesized only when both 6-AHA and PVP were added to the synthesis (FIG. 3 ). Accordingly, it was confirmed that when two compounds, 6-AHA and PVP, were complementarily participated in the synthesis and were applied simultaneously, nanocomplex having a stable size and dispersity as a biomaterial may be efficiently obtained.

Example 4: Change in Formation of Nanocomplex Depending on Amounts of PVP

In order to confirm the tendency of nanocomplex formation depending on the amounts of PVP serving as a dispersion stabilizer in the present disclosure, the change in the nanocomplex formation was examined by using PVP of various amounts of 1.0, 1.5, 2.0 and 2.5 g in the synthesis process of Example 1. As a result of analyzing the synthesized particle size through dynamic light scattering analysis, it was possible to obtain uniform particles of the smallest size when PVP was used in a dose of 2.0 g (19 mg/ml). Considering the effect of the size of the nanocomplex on dispersity, function and biological stability, it can be said that this is the result of finding for the most suitable synthesis conditions.

Example 5: Size Formation Trend of Cerium Oxide Nanocomplex Depending On Synthesis Time

In order to identify the particle size and stability of the cerium oxide nanocomplex that may be synthesized through Example 1 for each synthesis retention time, while the reaction of the fifth solution was maintained, samples were taken every 30, 40, 50, 60, 70, 80, 90, and 120 minutes, and the particle size was analyzed using dynamic light scattering device. As a result, it was confirmed that as the reaction time elapsed, the particle size gradually decreased from 30 nm to 5 nm, and each sample collected for each time had a very stable particle size. Therefore, it was confirmed that the method of the present disclosure is a process capable of manufacturing nanoparticles with remarkably excellent uniformity (FIG. 5 ).

Example 6: Coating of Cerium Oxide Nanocomplex With Biodispersion Stabilizer

A suspension was prepared by adding 3.5 mg of cerium oxide nanoparticles prepared through the above-mentioned process to 0.8 mL of sodium acetate buffer (2.5 mM). The suspension was mixed with 0.3 µmol of polyglutamic acid (PLGA) (weight average molecular weight: 9,000) or the same weight of polyvinyl alcohol (PVA) (weight average molecular weight: 9,500) and dextran (weight average molecular weight: 6,000) dissolved in 1.2 mL of sodium acetate buffer. The cerium oxide nanocomplex was obtained by stirring the mixture at room temperature for 5 minutes and combining positively charged 6-AHA bound to the surface of the cerium oxide nanoparticles and surface negatively charged the polyglutamic acid, polyvinyl alcohol, dextran, etc., by electrostatic attraction.

It was confirmed that the cerium oxide nanocomplex had a surface potential value of 5 mV before coating with a biocompatible dispersion stabilizer, and had a charge value of -40 mV after coating with PLGA, and a charge value close to -1 mV after coating with PVA and dextran, respectively. Also, it was confirmed that different biocompatible dispersion stabilizers were coated on the cerium oxide nanoparticles through this method (FIG. 6A).

It was confirmed that in a dispersing environment of normal saline (an aqueous 0.9% (w/w) sodium chloride solution) that simulates the environment for use in actual biomedical applications, the cerium oxide nanocomplex had a size of 50 to 100 nm before coating with the biocompatible dispersion stabilizer, and the dispersion size was improved from 10 to 50 nm in all conditions using each dispersion stabilizer after coating with the biocompatible dispersion stabilizer (FIG. 6B).

Example 7: Evaluation of Antioxidant Effect of Cerium Oxide Nanocomplex

In order to determine the antioxidant effect of the cerium oxide nanocomplex coated with different biocompatible dispersion stabilizers, the scavenging of representative reactive oxygen species, hydrogen peroxide (H₂O₂) and hydroxyl radicals (-OH), was investigated. For the analysis of each reactive oxygen species, an AmplexTM Red Hydergen Peroxide/Peroxidase Assay Kit was used for hydrogen peroxide, and hydroxyl radical antioxidant capacity (HORAC) assay was used for hydroxyl radicals. It was confirmed through each analysis that the cerium oxide nanocomplex not only had the function of scavenging various types of reactive oxygen species, but also that this function was proportional to the concentration of the particles (FIG. 7 ). In addition, it could be confirmed that although the cerium oxide nanocomplex was coated with different kinds of dispersion stabilizers, the ability to scavenge reactive oxygen species was derived from the core particles by successfully scavenging reactive oxygen species.

Experimental Example 1: Treatment Effect of Cerium Oxide Nanocomplex For Bowel Perforation Peritonitis

In order to confirm the therapeutic effect of cerium oxide nanocomplex in the present disclosure for bowel perforation peritonitis, a model of cecal ligation and puncture (CLP) was prepared using C57BL/6 mice. Specifically, C57BL/6 mice were anesthetized with isoflurane, disinfected with a betadine solution (10% povidone-iodine) after abdominal hair removal. Then a midline skin incision was made to expose the appendix. The half point between the ileocecal valve and the end of the appendix was ligated with 6-0 black silk. The half point between the ligation site and the end of the appendix was punctured with a 26G needle and confirmed the spillage of intestinal contents. The appendix was relocated into the abdominal cavity, and the surgical incision was sutured and disinfected. Immediately after inducing bowel perforation peritonitis, 0.5 mg/kg of the cerium oxide nanocomplex of the present disclosure was intravenously injected once into the tail vein, or the same volume of saline was intravenously injected to the control group. Until 14 days from the time when bowel perforation peritonitis was induced, the death or life of the above mice was checked and their survival rate was measured (FIG. 8 ). As a result, it was confirmed that the survival rate of mice injected with the cerium oxide nanocomplex of the present disclosure significantly increased compared with that of the control group. Specifically, the survival rate of control group recorded 13.3% (n=15) whereas the survival rate of the group injected with the cerium oxide nanocomplex recorded a whopping 53.3% (n=15), which is a statistically significant result (P=0.03).

Experimental Example 2: Treatment Effect of Cerium Oxide Nanocomplex For Bowel Perforation Peritonitis Evaluated Through Clinical Symptom Scores

The mice in the above experimental example 1 were observed every day and their clinical symptom scores calculated by taking the sum of values for the observed symptoms in table 1 below.

TABLE 1 Symptom Score 0 1 activity normal lethargic piloerection normal ruffled tremor no tremor shaky eye normal exudate respiration normal labored stool hard loose to liquid

Clinical score calculated for living mice has a range between 0 and 6 whereby 0 means a normal condition and 6 means the most severe condition. As seen in FIG. 9 , the clinical symptom scores of mice injected with cerium oxide nanocomplex of the present disclosure remarkably improved for 14 days compared with the control group.

From the above result, it was confirmed that the cerium oxide nanocomplex of the present disclosure not only improves the survival rate of mice model of bowel perforation peritonitis but also significantly improves clinical symptoms of living animals.

Specific portions of the present disclosure have been described in detail hereinabove, but it is obvious to those skilled in the art that such a specific description is only an exemplary embodiment, and the scope of the present disclosure is not limited thereto. Therefore, the substantial scope of the present disclosure will be defined by the claims and equivalents thereof. 

1. A cerium oxide nanocomplex comprising: (a) core layer of cerium oxide nanoparticles; and (b) an inner layer including a polymer represented by the following Formula 1:

wherein R₁ and R₂ are each independently hydrogen or oxygen, represents a single bond or a double bond, l is 1 or 2, and m is an integer of 100 to
 1000. 2. The nanocomplex of claim 1, wherein the cerium oxide nanoparticles are selected from the group consisting of cerium(III) oxide (Ce₂O₃) nanoparticles, cerium(IV) oxide (CeO₂) nanoparticles, and a mixture thereof.
 3. The nanocomplex of claim 1, wherein in Formula 1, R₁ is hydrogen, R₂ is oxygen, and l is
 1. 4. The nanocomplex of claim 1, wherein the nanocomplex further comprises an outer layer that comprises one or more of biocompatible dispersion stabilizers selected from the group consisting of polyglutamic acid (PGA), poly(aspartic acid) (PASP), alginate, poly(acrylic acid) (PAA), poly(methacrylic acid) (PMAA), poly(methyl methacrylic acid), poly(maleic acid) (PMA), poly (butadiene/maleic acid) (PBMA), poly (vinylphosphonic acid) (PSSA), polyvinyl alcohol (PVA) and dextran.
 5. The nanocomplex of claim 4, wherein the biocompatible dispersion stabilizer included in the outer layer is polyglutamic acid (PGA).
 6. The nanocomplex of claim 5, wherein the PGA is poly L-glutamic acid (PLGA).
 7. The nanocomplex of claim 1, further comprising a multifunctional ligand represented by the following Formula 2:

wherein n is an integer of 3 to
 7. 8. The nanocomplex of claim 7, wherein in Formula 2, n is
 5. 9. The nanocomplex of claim 1, wherein the nanocomplex has an average particle size of 5 nm to 100 nm.
 10. A method for preventing or treating peritonitis comprising administering the nanocomplex of claim 1 to a subject in need thereof.
 11. The method of claim 1, wherein the peritonitis is caused by perforation in an organ of abdominal cavity, selected from the group consisting of esophagus, stomach, duodenum, small intestine, large intestine, appendix and gallbladder.
 12. A method for preventing or treating peritonitis comprising administering the nanocomplex of claim 2 to a subject in need thereof.
 13. A method for preventing or treating peritonitis comprising administering the nanocomplex of claim 3 to a subject in need thereof.
 14. A method for preventing or treating peritonitis comprising administering the nanocomplex of claim 4 to a subject in need thereof.
 15. A method for preventing or treating peritonitis comprising administering the nanocomplex of claim 5 to a subject in need thereof.
 16. A method for preventing or treating peritonitis comprising administering the nanocomplex of claim 6 to a subject in need thereof.
 17. A method for preventing or treating peritonitis comprising administering the nanocomplex of claim 7 to a subject in need thereof.
 18. A method for preventing or treating peritonitis comprising administering the nanocomplex of claim 8 to a subject in need thereof.
 19. A method for preventing or treating peritonitis comprising administering the nanocomplex of claim 9 to a subject in need thereof. 